Material Group | P - Steel |
Sub-Group | Low Carbon Steel |
Tensile Strength | 750 [N/mm^2] |
Machinability | 65% - 80% |
Standard | Name |
---|---|
sae | A27 65.35 |
wnr | 1.0443 |
din | GS.45 |
bs | A1 |
ss | 1305 |
anfor | E23.45M |
unf | F.221 |
Element | Amount |
---|---|
Silicon (Si) | 0.8% |
Manganese (Mn) | 0.7% |
Carbon (C) | 0.3% |
Phosphorus (P) | 0.04% |
Sulfur (S) | 0.035% |
Application | Vc (m/min) | Vc (SFM) |
---|---|---|
Turning | 285-350 | 930-1150 |
Milling | 175-220 | 570-720 |
Parting | 135-170 | 440-560 |
Grooving | 160-195 | 520-640 |
Drilling | 115-140 | 380-460 |
Honing Siz | 0.05-0.08 mm / 0.002-0.003" |
Rake Angl | 11° -13° |
Land Angl | Positive |
Land Widt | 0.20-0.30 mm / 0.008-0.012" |